PA612 GF25

PA610 GF25 is a type of comound plastic material called a nylon 610 reinforced with 25% glass fiber. This reinforcement with glass fibers makes the material stronger and more rigid than regular nylon 610.

GET FREE QUOTATION

Breif Introduction of PA612 GF25

PA612 GF25 is a modified plastic material belonging to the polyamide 612 (nylon 612) family, reinforced with 25% glass fiber. This reinforcement significantly enhances its properties compared to its unreinforced counterpart. Key improvements include:

Increased Tensile Strength: PA612 GF25 exhibits superior resistance to pulling forces, making it suitable for applications requiring high load-bearing capabilities.
Enhanced Stiffness: The addition of glass fibers translates to greater rigidity, making the material ideal for components needing dimensional stability under pressure.
Improved Dimensional Stability: PA612 GF25 maintains its shape better under varying temperatures and loads compared to unreinforced nylon 610.

These combined improvements make PA612GF25 a versatile material for various applications across industries. It’s commonly used in:

Automotive Parts: Due to its strength and heat resistance, PA612 GF25 finds application in engine components, gears, and structural parts.
Electrical Components: Its good electrical insulating properties make it suitable for electrical housings and connectors.
Industrial Applications: PA612 GF25’s strength and dimensional stability are beneficial for gears, bearings, and machine parts.

It’s important to consider variations within the PA6 nylon family. For example, PA612 GF25 and PA612-GF25 represent similar materials, but with nylon 612 (polyamide 612) as the base plastic. PA612 might offer slightly different properties like a higher melting point or enhanced chemical resistance compared to PA610.

Finally, PA610 GF25 and PA612 GF33 might seem similar due to the “GF25” designation, but the latter boasts a higher glass fiber content of 33%. This translates to even greater strength and stiffness but might affect other characteristics like impact resistance and ease of processing compared to PA610 GF25.

Application Industry of PA612 GF25

Car Accessories

Rocket Tail

Ammunition Box

PA612 GF25 Data

Rheological properties	dry / cond	Unit	Test Standard
Melt volume-flow rate, MVR	80 / *	cm³/10min	ISO 1133
Temperature	275 / *	°C	ISO 1133
Load	21.6 / *	kg	ISO 1133
Molding shrinkage, parallel	0.3 / *	%	ISO 294-4, 2577
Molding shrinkage, normal	0.8 / *	%	ISO 294-4, 2577

Mechanical properties	dry / cond	Unit	Test Standard
Tensile modulus	6800 / –	MPa	ISO 527-1/-2
Yield stress	120 / –	MPa	ISO 527-1/-2
Yield strain	3.6 / –	%	ISO 527-1/-2
Nominal strain at break	4.6 / –	%	ISO 527-1/-2
Charpy impact strength, +23°C	75C / —	kJ/m²	ISO 179/1eU
Charpy impact strength, -30°C	70C / —	kJ/m²	ISO 179/1eU
Charpy notched impact strength, +23°C	10C / —	kJ/m²	ISO 179/1eA
Charpy notched impact strength, -30°C	11C / —	kJ/m²	ISO 179/1eA

Thermal properties	dry / cond	Unit	Test Standard
Melting temperature, 10°C/min	178 / *	°C	ISO 11357-1/-3
Temp. of deflection under load, 1.80 MPa	170 / *	°C	ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa	175 / *	°C	ISO 75-1/-2
Vicat softening temperature, 50°C/h 50N	170 / *	°C	ISO 306
Coeff. of linear therm. expansion, parallel	100 / *	E-6/K	ISO 11359-1/-2
Coeff. of linear therm. expansion, normal	80 / *	E-6/K	ISO 11359-1/-2
Burning behavior at 1.5 mm nominal thickness	HB / *	class	IEC 60695-11-10
Thickness tested (1.5)	1.6 / *	mm	IEC 60695-11-10
Yellow Card available	Yes / *	–	–
Burning behavior at thickness h	HB / *	class	IEC 60695-11-10
Thickness tested (h)	0.8 / *	mm	IEC 60695-11-10
Yellow Card available	Yes / *	–	–

Electrical properties	dry / cond	Unit	Test Standard
Volume resistivity	21 / –	Ohm*m	IEC 62631-3-1

Other properties	dry / cond	Unit	Test Standard
Water absorption	1.2 / *	%	Sim. to ISO 62
Humidity absorption	0.5 / *	%	Sim. to ISO 62
Density	1270 / –	kg/m³	ISO 1183