PA12 compound resin builds on the strengths of PA12 resin by adding fillers or additives. This enhances properties like flame retardancy, electrical conductivity, or specific colors. It offers a wider range of performance possibilities.

Item No.: PA12 A-1

Värv: must

SAADA TASUTA HINNAPAKKUMINE

Breif Introduction of PA12 Compound Resin

PA12 compound resin takes the strong foundation of PA12 material, also known as Nylon 12, and elevates its capabilities by incorporating fillers and additives. These enhancements cater to specific needs, such as improved flame retardancy, increased electrical conductivity, or achieving desired colors.

A common example is PA12 CF, which introduces carbon fiber reinforcement. This significantly boosts the strength and stiffness of the compound resin. Compared to standard PA12 material, PA12 compound resin offers a broader spectrum of performance possibilities, making it a versatile material for various applications.

One such application is PA12 extrusion. By using PA12 compound resin in extrusion processes, manufacturers can create parts with tailored properties. For instance, flame-retardant additives can be incorporated for applications requiring enhanced fire safety.

Overall, PA12 compound resin provides greater flexibility and control compared to base PA12 material. This allows manufacturers to achieve specific performance requirements for diverse end products in industries like automotive, aerospace, and consumer goods.

Application Industry of PA12 Compound Resin

Satellite Parts

Ehitusmaterjal

Medical Filter

PA12 Compound Resin Data

Reoloogilised omadused	kuiv / kond	Üksus	Katse Standard
Sulamise mahu-voolukiirus, MVR	25 / *	cm³/10min	ISO 1133
Temperatuur	275 / *	°C	ISO 1133
Koormus	5 / *	kg	ISO 1133
Vormimise kokkutõmbumine, paralleelne	0.7 / *	%	ISO 294-4, 2577
Vormimise kokkutõmbumine, normaalne	1.3 / *	%	ISO 294-4, 2577

Mehaanilised omadused	kuiv / kond	Üksus	Katse Standard
Tõmbemoodul	1550 / 1300	MPa	ISO 527-1/-2
Mahtuvuspinge	46 / 42	MPa	ISO 527-1/-2
Tüve saagikus	4 / 12	%	ISO 527-1/-2
Nominaalne tüvi purunemisel	>50 / >50	%	ISO 527-1/-2
Löögitugevus Charpy, +23°C	N / N	kJ/m²	ISO 179/1eU
Löögitugevus Charpy, -30°C	N / N	kJ/m²	ISO 179/1eU
Löögitugevus Charpy, +23°C	10C / 12C	kJ/m²	ISO 179/1eA
Löögitugevus Charpy, -30°C	8C / 8C	kJ/m²	ISO 179/1eA

Soojusomadused	kuiv / kond	Üksus	Katse Standard
Sulamistemperatuur, 10°C/min	178 / *	°C	ISO 11357-1/-3
Paindumise tempo koormuse all, 1,80 MPa	50 / *	°C	ISO 75-1/-2
Paindumise tempo koormuse all, 0,45 MPa	110 / *	°C	ISO 75-1/-2
Vicat pehmenemistemperatuur, 50°C/h 50N	140 / *	°C	ISO 306
Lineaarse soojuspaisumise koefitsient, paralleelne	150 / *	E-6/K	ISO 11359-1/-2
Põlemiskäitumine 1,5 mm nimipaksuse juures	HB / *	klass	IEC 60695-11-10
Testitud paksus (1,5)	1.6 / *	mm	IEC 60695-11-10

Elektrilised omadused	kuiv / kond	Üksus	Katse Standard
Relative permittivity, 100Hz	9.7 / 5	–	IEC 62631-2-1
Relative permittivity, 1MHz	4 / 3.5	–	IEC 62631-2-1
Dissipation factor, 100Hz	2100 / 1000	E-4	IEC 62631-2-1
Dissipation factor, 1MHz	1100 / 500	E-4	IEC 62631-2-1
Mahutugevus	1E10 / 5E10	Ohm*m	IEC 62631-3-1
Pinna eritakistus	* / 6E14	Ohm	IEC 62631-3-2
Elektriline tugevus	39 / 35	kV/mm	IEC 60243-1
Võrdlev jälgimisindeks	600 / 600	–	IEC 60112

Muud omadused	kuiv / kond	Üksus	Katse Standard
Vee imendumine	1.5 / *	%	Sarnaselt ISO 62-le
Niiskuse neeldumine	0.7 / *	%	Sarnaselt ISO 62-le
Tihedus	1010 / 1020	kg/m³	ISO 1183