PA12 resin is a high-performance plastic known for its exceptional strength, toughness, and durability. It’s a type of nylon resin, also called Nylon 12, and is valued for its resistance to chemicals, abrasion, and low temperatures.

Item No.: PA12 MA01

Color: Black

ZÍSKAT BEZPLATNOU NABÍDKU

Breif Introduction of PA12 Resin

PA12 resin, also known as nylon PA12, is a high-performance plastic belonging to the polyamide family. Compared to its close relative, PA6 (nylon 6), PA12 offers several advantages. PA12 resin demonstrates superior low-temperature performance, making it ideal for applications in cold environments. Additionally, it boasts higher impact strength and better resistance to chemicals.

Here’s a closer look at how PA12 resin compares to PA6:

Výkon při nízkých teplotách: PA12 excels in cold environments, remaining flexible and functional at much lower temperatures than PA6.
Impact strength: PA12 resin offers superior impact resistance, making it more resistant to shocks and fractures.
Chemická odolnost: PA12 exhibits better resistance to a wider range of chemicals compared to PA6.

However, there are also some trade-offs to consider between PA12 resin and PA6:

Melting temperature: PA12 has a lower melting temperature compared to PA6. This can limit its use in high-heat applications.
Náklady: PA12 resin is generally more expensive than PA6.

In conclusion, when choosing between PA12 resin and PA6, the deciding factor often comes down to the specific application’s requirements. If low-temperature performance, impact strength, and chemical resistance are critical, PA12 resin might be the better choice. However, if cost or high-heat resistance is a major concern, PA6 might be a more suitable option.

Application Industry of PA12 Resin

Automobile Manufacturing

Fitness Equipment

Tubing

PA12 Resin Data

Fyzikální vlastnosti	Metrické	Angličtina	Komentáře
Specifická hmotnost	1.02 g/cc	1.02 g/cc	ASTM D792
Absorpce vody	0.30 %	0.30 %	24 hodin při 23 °C; ASTM D570
Lineární smrštění formy	0.015 cm/cm Tloušťka 3,17 mm	0.015 in/in @Tloušťka 0,125 palce	ASTM D955
	0.020 cm/cm @Tloušťka 6,35 mm	0.020 in/in @Tloušťka 0,250 palce	ASTM D955

Mechanické vlastnosti	Metrické	Angličtina	Komentáře
Tvrdost, Rockwell R	108	108	ASTM D785
Pevnost v tahu, mez pevnosti	44.8 MPa	6500 psi	ASTM D638
Prodloužení při přetržení	>= 10 %	>= 10 %	ASTM D638
Modul pružnosti	1,38 GPa	200 ksi	ASTM D638
Pevnost v tahu za ohybu	51,7 MPa	7500 psi	ASTM D790
Modul pružnosti v ohybu	1,38 GPa	200 ksi	ASTM D790
Izod Impact, vroubkované	0,481 J/cm Tloušťka 3,17 mm	0,900 ft-lb/in @Tloušťka 0,125 palce	ASTM D256
Izod Impact, bez zářezů	16,0 J/cm Tloušťka 3,17 mm	30,0 ft-lb/in @Tloušťka 0,125 palce	ASTM D256

Elektrické vlastnosti	Metrické	Angličtina	Komentáře
Elektrický odpor	1,00e+12 ohm-cm	1,00e+12 ohm-cm	ASTM D257

Tepelné vlastnosti	Metrické	Angličtina	Komentáře
Teplota průhybu při tlaku 0,46 MPa (66 psi)	138 °C	280 °F	ASTM D648
Teplota průhybu při tlaku 1,8 MPa (264 psi)	51.7 °C	125 °F	ASTM D648
Hořlavost, UL94	HB @Tloušťka 1,59 mm	HB @Tloušťka 0,0625 palce	Podle testů společnosti RTP Company; ASTM D635

Vlastnosti zpracování	Metrické	Angličtina	Komentáře
Teplota zpracování	216 - 266 °C	420 - 510 °F
Teplota formy	65.6 - 104 °C	150 - 220 °F
Vstřikovací tlak	68,9 - 103 MPa	10000 - 15000 psi