In addition to the characteristics of high strength, wear resistance and oil resistance, PA610 natural resin also has low water absorption, good dimensional stability, and excellent electrical properties.
ZÍSKAT BEZPLATNOU NABÍDKUPA610 natural resin, also known as polyamide 610, is a high-performance plastic known for its exceptional combination of mechanical properties. It boasts superior strength and stiffness, making it ideal for demanding applications.
PA610 shines in high-heat environments due to its excellent thermal resistance, which allows it to maintain its shape and performance at elevated temperatures. An additional benefit is its inherent flame retardancy, making it a suitable choice for safety-critical applications. Furthermore, PA610 offers good chemical resistance to various oils, greases, and fuels, enhancing its versatility. Finally, this resin exhibits good dimensional stability, minimizing warping or shrinkage over time.
Overall, PA610 natural resin is a compelling choice for components requiring a balance of strength, heat tolerance, flame retardancy, and chemical resistance.
| Fyzikální vlastnosti | Metrické | Angličtina | Komentáře | ||
|---|---|---|---|---|---|
| Specifická hmotnost | 1.08 g/cc | 1.08 g/cc | ASTM D792 | ||
| Absorpce vody | 0.40 % | 0.40 % | 24 hodin při 23 °C; ASTM D570 | ||
Lineární smrštění formy  | 0.015 cm/cm Tloušťka 3,17 mm | 0.015 in/in @Tloušťka 0,125 palce | ASTM D955 | ||
| 0.020 cm/cm @Tloušťka 6,35 mm | 0.020 in/in @Tloušťka 0,250 palce | ASTM D955 | |||
| Mechanické vlastnosti | Metrické | Angličtina | Komentáře | ||
| Tvrdost, Rockwell R | 111 | 111 | ASTM D785 | ||
| Pevnost v tahu, mez pevnosti | 62.1 MPa | 9000 psi | ASTM D638 | ||
| Prodloužení při přetržení | 90 % | 90 % | ASTM D638 | ||
| Modul pružnosti | 2.76 GPa | 400 ksi | ASTM D638 | ||
| Pevnost v tahu za ohybu | 86.2 MPa | 12500 psi | ASTM D790 | ||
| Modul pružnosti v ohybu | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Pevnost v tlaku | 68.9 MPa | 10000 psi | ASTM D695 | ||
| Izod Impact, vroubkované | 0,481 J/cm Tloušťka 3,17 mm | 0,900 ft-lb/in @Tloušťka 0,125 palce | ASTM D256 | ||
| Izod Impact, bez zářezů | 6.41 J/cm Tloušťka 3,17 mm | 12.0 ft-lb/in @Tloušťka 0,125 palce | ASTM D256 | ||
| Elektrické vlastnosti | Metrické | Angličtina | Komentáře | ||
| Elektrický odpor | 1,00e+12 ohm-cm | 1,00e+12 ohm-cm | ASTM D257 | ||
| Dielektrická konstanta | 3.1 @Frekvence 1e+6 Hz | 3.1 @Frekvence 1e+6 Hz | Suchý; ASTM D150 | ||
| Dielektrická pevnost | 19.7 kV/mm | 500 kV/in | S/T; ASTM D149 | ||
| Rozptylový faktor | 0.020 @Frekvence 1e+6 Hz | 0.020 @Frekvence 1e+6 Hz | Suchý; ASTM D150 | ||
| Odolnost proti oblouku | 120 sec | 120 sec | ASTM D495 | ||
| Tepelné vlastnosti | Metrické | Angličtina | Komentáře | ||
| CTE, lineární, paralelní k toku | 90.0 µm/m-°C @Teplota 20,0 °C | 50.0 µin/in-°F @Teplota 68,0 °F | ASTM D696 | ||
| Tepelná vodivost | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | Průchozí rovina; ASTM C177 | ||
| Teplota průhybu při tlaku 0,46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 | ||
| Teplota průhybu při tlaku 1,8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 | ||
| Hořlavost, UL94 | V-2 @Tloušťka 1,59 mm | V-2 @Tloušťka 0,0625 palce | Podle testů společnosti RTP Company; ASTM D3801 | ||
| Vlastnosti zpracování | Metrické | Angličtina | Komentáře | ||
| Teplota zpracování | 274 – 293 °C | 525 – 560 °F | |||
| Teplota formy | 65.6 – 107 °C | 150 – 225 °F | |||
| Vstřikovací tlak | 68.9 – 124 MPa | 10000 – 18000 psi | |||
| Popisné vlastnosti | |||||
| Barva | Natural/Black | ||||
Úvod Ve stále konkurenčním průmyslovém prostředí výběr materiálu často rozhoduje o úspěchu technických návrhů [...]
Představení plastů a plastových surovin Co je to plast a plastové suroviny? Plasty [...]
Nylon vs PTFE Nylon a PTFE (polytetrafluorethylen) jsou dva široce používané materiály, z nichž každý [...]
Úvod V našem moderním světě hrají specializované materiály, jako je PA6 GB20 GF10, zásadní roli při výrobě [...]
Nylon, široce používaný syntetický polymer, je oblíbený pro své [...]
Úvod Polyamid 11, běžně označovaný jako PA 11, je vysoce výkonná termoplastická pryskyřice odvozená z [...]
Úvod V dnešním průmyslovém prostředí může výběr správného materiálu znamenat zásadní rozdíl v [...]
Představení polyamidu vs. nylon V dnešním světě výroby a designu výrobků je výběr [...]
Bulgarian
Estonian
Turkish