PA12 Yhdistelmähartsi

PA12 compound resin builds on the strengths of PA12 resin by adding fillers or additives. This enhances properties like flame retardancy, electrical conductivity, or specific colors. It offers a wider range of performance possibilities.

Item No.: PA12 A-1

Väri: Musta

SAAT ILMAISEN TARJOUKSEN

Breif Introduction of PA12 Compound Resin

PA12 compound resin takes the strong foundation of PA12 material, also known as Nylon 12, and elevates its capabilities by incorporating fillers and additives. These enhancements cater to specific needs, such as improved flame retardancy, increased electrical conductivity, or achieving desired colors.

A common example is PA12 CF, which introduces carbon fiber reinforcement. This significantly boosts the strength and stiffness of the compound resin. Compared to standard PA12 material, PA12 compound resin offers a broader spectrum of performance possibilities, making it a versatile material for various applications.

One such application is PA12 extrusion. By using PA12 compound resin in extrusion processes, manufacturers can create parts with tailored properties. For instance, flame-retardant additives can be incorporated for applications requiring enhanced fire safety.

Overall, PA12 compound resin provides greater flexibility and control compared to base PA12 material. This allows manufacturers to achieve specific performance requirements for diverse end products in industries like automotive, aerospace, and consumer goods.

Application Industry of PA12 Compound Resin

Satellite Parts

Rakennusmateriaali

Medical Filter

PA12 Compound Resin Data

Reologiset ominaisuudet	kuiva / cond	Yksikkö	Testausstandardi
Sulan tilavuusvirta, MVR	25 / *	cm³/10min	ISO 1133
Lämpötila	275 / *	°C	ISO 1133
Lataa	5 / *	kg	ISO 1133
Muotin kutistuminen, samansuuntainen	0.7 / *	%	ISO 294-4, 2577
Muotin kutistuminen, normaali	1.3 / *	%	ISO 294-4, 2577

Mekaaniset ominaisuudet	kuiva / cond	Yksikkö	Testausstandardi
Vetomoduuli	1550 / 1300	MPa	ISO 527-1/-2
Myötöjännitys	46 / 42	MPa	ISO 527-1/-2
Tuottokanta	4 / 12	%	ISO 527-1/-2
Nimellinen murtovenymä	>50 / >50	%	ISO 527-1/-2
Charpy-iskulujuus, +23°C	N / N	kJ/m²	ISO 179/1eU
Charpy impact strength, -30°C	N / N	kJ/m²	ISO 179/1eU
Charpyn lovettu iskunkestävyys, +23°C	10C / 12C	kJ/m²	ISO 179/1eA
Charpyn lovettu iskunkestävyys, -30°C	8C / 8C	kJ/m²	ISO 179/1eA

Lämpöominaisuudet	kuiva / cond	Yksikkö	Testausstandardi
Sulamislämpötila, 10°C/min	178 / *	°C	ISO 11357-1/-3
Taivutuslämpötila kuormituksen alaisena, 1,80 MPa	50 / *	°C	ISO 75-1/-2
Taipuman lämpötila kuormituksen alaisena, 0,45 MPa	110 / *	°C	ISO 75-1/-2
Vicat-pehmenemislämpötila, 50°C/h 50N	140 / *	°C	ISO 306
Coeff. of linear therm. expansion, parallel	150 / *	E-6/K	ISO 11359-1/-2
Palamiskäyttäytyminen 1,5 mm:n nimellispaksuudella	HB / *	luokka	IEC 60695-11-10
Thickness tested (1.5)	1.6 / *	mm	IEC 60695-11-10

Sähköiset ominaisuudet	kuiva / cond	Yksikkö	Testausstandardi
Relative permittivity, 100Hz	9.7 / 5	–	IEC 62631-2-1
Relative permittivity, 1MHz	4 / 3.5	–	IEC 62631-2-1
Dissipation factor, 100Hz	2100 / 1000	E-4	IEC 62631-2-1
Dissipation factor, 1MHz	1100 / 500	E-4	IEC 62631-2-1
Tilavuusresistiivisyys	1E10 / 5E10	Ohm*m	IEC 62631-3-1
Pinnan resistiivisyys	* / 6E14	Ohm	IEC 62631-3-2
Sähköinen lujuus	39 / 35	kV/mm	IEC 60243-1
Vertaileva seurantaindeksi	600 / 600	–	IEC 60112

Muut ominaisuudet	kuiva / cond	Yksikkö	Testausstandardi
Veden imeytyminen	1.5 / *	%	Samanlainen kuin ISO 62
Kosteuden imeytyminen	0.7 / *	%	Samanlainen kuin ISO 62
Tiheys	1010 / 1020	kg/m³	ISO 1183