PA610 black resin is a type of high-performance plastic known for its durability and resistance to heat. It is a specific kind of polyamide, which is a family of engineering plastics. PA610 black resin is known for its exceptional mechanical properties, chemical resistance, and dimensional stability at elevated temperatures. This makes it a valuable material for a variety of applications in demanding environments.
PA610 black resin is a high-performance plastic belonging to the polyamide 610 family. It’s known for its exceptional mechanical properties, including strength and durability.
Additionally, it exhibits excellent resistance to chemicals and maintains its shape even at elevated temperatures. These qualities make PA610 black resin a valuable material for demanding applications across various industries. For instance, it’s commonly used in machinery manufacturing, oil storage containers, and textiles.
In the electronics industry, PA610 black resin finds uses in battery shells and instrument rails due to its durability and electrical properties. You might even encounter it in everyday objects like toothbrush bristles and cable coatings.
Fuchen always offer the PA610 resin in factory price. Let us know your requirement, we will give your our professional advice.
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 | ||
| Water Absorption | 0.40 % | 0.40 % | 24 hours at 23°C; ASTM D570 | ||
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.17 mm | 0.015 in/in @Thickness 0.125 in | ASTM D955 | ||
| 0.020 cm/cm @Thickness 6.35 mm | 0.020 in/in @Thickness 0.250 in | ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 111 | 111 | ASTM D785 | ||
| Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 | ||
| Elongation at Break | 90 % | 90 % | ASTM D638 | ||
| Modulus of Elasticity | 2.76 GPa | 400 ksi | ASTM D638 | ||
| Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 | ||
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Compressive Yield Strength | 68.9 MPa | 10000 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm | 0.900 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Izod Impact, Unnotched | 6.41 J/cm @Thickness 3.17 mm | 12.0 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | Dry; ASTM D150 | ||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | S/T; ASTM D149 | ||
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | Dry; ASTM D150 | ||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | Through-plane; ASTM C177 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 | ||
| Flammability, UL94 | V-2 @Thickness 1.59 mm | V-2 @Thickness 0.0625 in | Per testing by RTP Company; ASTM D3801 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 274 – 293 °C | 525 – 560 °F | |||
| Mold Temperature | 65.6 – 107 °C | 150 – 225 °F | |||
| Injection Pressure | 68.9 – 124 MPa | 10000 – 18000 psi | |||
| Descriptive Properties | |||||
| Color | Black | ||||
Introduction In the world of engineering plastics, nylon materials, particularly PA66, have carved out a [...]
Introduction of Nylon Polymer Thermal Conductivity Thermal conductivity is a fundamental property that dictates how [...]
Introduction ABS (Acrylonitrile Butadiene Styrene) plastic is a cornerstone material in modern manufacturing, renowned for [...]
Introduction Nylon, a revolutionary synthetic polymer, has reshaped industries with its unique blend of strength, [...]
Introduction Reinforced nylon stands as a testament to how material engineering can transform industries. By [...]
Introduction When it comes to engineering plastics, two of the most commonly used materials are [...]
Introduction Nylon is one of the most versatile and widely used synthetic polymers, and among [...]