In addition to the characteristics of high strength, wear resistance and oil resistance, PA610 natural resin also has low water absorption, good dimensional stability, and excellent electrical properties.
ZÍSKAJTE BEZPLATNÚ PONUKUPA610 natural resin, also known as polyamide 610, is a high-performance plastic known for its exceptional combination of mechanical properties. It boasts superior strength and stiffness, making it ideal for demanding applications.
PA610 shines in high-heat environments due to its excellent thermal resistance, which allows it to maintain its shape and performance at elevated temperatures. An additional benefit is its inherent flame retardancy, making it a suitable choice for safety-critical applications. Furthermore, PA610 offers good chemical resistance to various oils, greases, and fuels, enhancing its versatility. Finally, this resin exhibits good dimensional stability, minimizing warping or shrinkage over time.
Overall, PA610 natural resin is a compelling choice for components requiring a balance of strength, heat tolerance, flame retardancy, and chemical resistance.
| Fyzikálne vlastnosti | Metrické | Angličtina | Komentáre | ||
|---|---|---|---|---|---|
| Špecifická hmotnosť | 1.08 g/cc | 1.08 g/cc | ASTM D792 | ||
| Absorpcia vody | 0.40 % | 0.40 % | 24 hours at 23°C; ASTM D570 | ||
Lineárne zmrštenie formy  | 0.015 cm/cm @ Hrúbka 3,17 mm | 0.015 in/in Hrúbka 0,125 palca | ASTM D955 | ||
| 0.020 cm/cm @Thickness 6.35 mm | 0.020 in/in @Thickness 0.250 in | ASTM D955 | |||
| Mechanické vlastnosti | Metrické | Angličtina | Komentáre | ||
| Tvrdosť, Rockwell R | 111 | 111 | ASTM D785 | ||
| Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 | ||
| Predĺženie pri pretrhnutí | 90 % | 90 % | ASTM D638 | ||
| Modul pružnosti | 2.76 GPa | 400 ksi | ASTM D638 | ||
| Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 | ||
| Modul pružnosti v ohybe | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Compressive Yield Strength | 68.9 MPa | 10000 psi | ASTM D695 | ||
| Izod Impact, vrúbkovaný | 0.481 J/cm @ Hrúbka 3,17 mm | 0.900 ft-lb/in Hrúbka 0,125 palca | ASTM D256 | ||
| Izod Impact, bez zárezov | 6.41 J/cm @ Hrúbka 3,17 mm | 12.0 ft-lb/in Hrúbka 0,125 palca | ASTM D256 | ||
| Elektrické vlastnosti | Metrické | Angličtina | Komentáre | ||
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | Dry; ASTM D150 | ||
| Dielektrická pevnosť | 19.7 kV/mm | 500 kV/in | S/T; ASTM D149 | ||
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | Dry; ASTM D150 | ||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Tepelné vlastnosti | Metrické | Angličtina | Komentáre | ||
| CTE, lineárna, paralelná k toku | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Tepelná vodivosť | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | Through-plane; ASTM C177 | ||
| Teplota vychýlenia pri tlaku 0,46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 | ||
| Teplota vychýlenia pri tlaku 1,8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 | ||
| Horľavosť, UL94 | V-2 @Thickness 1.59 mm | V-2 @Thickness 0.0625 in | Per testing by RTP Company; ASTM D3801 | ||
| Vlastnosti spracovania | Metrické | Angličtina | Komentáre | ||
| Processing Temperature | 274 – 293 °C | 525 – 560 °F | |||
| Teplota formy | 65.6 – 107 °C | 150 – 225 °F | |||
| Injection Pressure | 68.9 – 124 MPa | 10000 – 18000 psi | |||
| Opisné vlastnosti | |||||
| Color | Natural/Black | ||||
Úvod 3D tlač sa stala základným nástrojom pre nadšencov, inžinierov aj výrobcov. Či už ide o [...]
Úvod Nylon je jedným z najuniverzálnejších technických plastov používaných v širokom spektre [...]
Úvod Nylon je názov, ktorý sa objavuje všade v našom každodennom živote, od oblečenia [...]
Úvod Nylon je jedným z najuniverzálnejších a najpoužívanejších syntetických polymérov v [...]
Úvod Vo svete technických plastov si nylónové materiály, najmä PA66, vydobyli [...]
Úvod do tepelnej vodivosti nylonových polymérov Tepelná vodivosť je základná vlastnosť, ktorá určuje, ako [...]
Úvod Plast ABS (akrylonitrilbutadiénstyrén) je základným materiálom v modernej výrobe, ktorý je známy svojimi [...]
Úvod Nylon, revolučný syntetický polymér, zmenil podobu priemyselných odvetví vďaka svojej jedinečnej kombinácii pevnosti, [...]
Bulgarian
Estonian
Turkish