PA12 harts

PA12 harts 

PA12 resin is a high-performance plastic known for its exceptional strength, toughness, and durability. It’s a type of nylon resin, also called Nylon 12, and is valued for its resistance to chemicals, abrasion, and low temperatures.

Item No.: PA12 MA01

Färg: Svart

FÅ GRATIS OFFERT

Breif Introduction of PA12 Resin

PA12 resin, also known as nylon PA12, is a high-performance plastic belonging to the polyamide family. Compared to its close relative, PA6 (nylon 6), PA12 offers several advantages. PA12 resin demonstrates superior low-temperature performance, making it ideal for applications in cold environments. Additionally, it boasts higher impact strength and better resistance to chemicals.

Here’s a closer look at how PA12 resin compares to PA6:

  • Prestanda vid låga temperaturer: PA12 excels in cold environments, remaining flexible and functional at much lower temperatures than PA6.
  • Impact strength: PA12 resin offers superior impact resistance, making it more resistant to shocks and fractures.
  • Kemisk beständighet: PA12 exhibits better resistance to a wider range of chemicals compared to PA6.

However, there are also some trade-offs to consider between PA12 resin and PA6:

  • Melting temperature: PA12 has a lower melting temperature compared to PA6. This can limit its use in high-heat applications.
  • Kostnad: PA12 resin is generally more expensive than PA6.

In conclusion, when choosing between PA12 resin and PA6, the deciding factor often comes down to the specific application’s requirements. If low-temperature performance, impact strength, and chemical resistance are critical, PA12 resin might be the better choice. However, if cost or high-heat resistance is a major concern, PA6 might be a more suitable option.

Application Industry of PA12 Resin

Automobile Manufacturing

Automobile Manufacturing

Fitness Equipment

Fitness Equipment

Tubing

Tubing

PA12 Resin Data

Fysikaliska egenskaperMetriskEngelskaKommentarer
Specifik gravitation 1.02 g/cc1.02 g/ccASTM D792
Absorption av vatten 0.30 %0.30 %24 timmar vid 23°C; ASTM D570
Linjär formkrympning 0,015 cm/cm
@Tjocklek 3,17 mm
0,015 tum/in
@Tjocklek 0,125 tum
ASTM D955
 0,020 cm/cm
@Tjocklek 6,35 mm
0,020 tum/in
@Tjocklek 0,250 tum
ASTM D955
 
Mekaniska egenskaperMetriskEngelskaKommentarer
Hårdhet, Rockwell R 108108ASTM D785
Draghållfasthet, ultimat 44.8 MPa6500 psiASTM D638
Töjning vid brott >= 10 %>= 10 %ASTM D638
Elasticitetsmodul 1.38 GPa200 ksiASTM D638
Böjhållfasthet 51.7 MPa7500 psiASTM D790
Böjmodul 1.38 GPa200 ksiASTM D790
Izod Impact, hackad 0,481 J/cm
@Tjocklek 3,17 mm
0,900 ft-lb/in
@Tjocklek 0,125 tum
ASTM D256
Izod Impact, ej avbruten 16,0 J/cm
@Tjocklek 3,17 mm
30,0 ft-lb/in
@Tjocklek 0,125 tum
ASTM D256
 
Elektriska egenskaperMetriskEngelskaKommentarer
Elektrisk resistivitet 1,00e+12 ohm-cm1,00e+12 ohm-cmASTM D257
 
Termiska egenskaperMetriskEngelskaKommentarer
Nedböjningstemperatur vid 0,46 MPa (66 psi) 138 °C280 °FASTM D648
Böjningstemperatur vid 1,8 MPa (264 psi) 51.7 °C125 °FASTM D648
Brandfarlighet, UL94 HB
@Tjocklek 1,59 mm
HB
@Tjocklek 0,0625 tum
Per testing by RTP Company; ASTM D635
 
BearbetningsegenskaperMetriskEngelskaKommentarer
Bearbetningstemperatur 216 – 266 °C420 – 510 °F 
Formtemperatur 65.6 – 104 °C150 – 220 °F 
Insprutningstryck 68.9 – 103 MPa10000 – 15000 psi

Relaterade bloggar

Modified Nylon: The Innovation Engine of High-performance Engineering Plastics

Introduction In 2023, the global modified nylon market size will exceed US$82 billion, of which [...]

De mångsidiga användningsområdena för PMMA-ark i olika branscher

Inledning Polymetylmetakrylat (PMMA)-skivor, ofta kända som akrylskivor eller plexiglas, har blivit en [...].

Vilka är 5 egenskaper hos nylon?

Introduktion av egenskaper hos Nylon Nylon är ett kraftfullt material som har format industrier och [...]].

Vilken är den viktigaste komponenten i nylon?

Introduktion av förening i nylon Nylon är ett av de mest revolutionerande syntetiska materialen någonsin [...]].

Vad är nylonchips? Användningar och fördelar du behöver känna till

Inledning Nylonchips är en viktig komponent i modern tillverkning och är kända för sina mångsidiga användningsområden [...].

Temperatur för utskrift av nylon: Hemligheten med Nylon 3D-utskrift

Inledning I 3D-utskriftsvärlden finns det ett material som utmärker sig genom sin mångsidighet och [...].

Nylon vs PETG: Vilket filament för 3D-utskrift är det bästa?

Inledning 3D-utskrift har blivit ett viktigt verktyg för både hobbyister, ingenjörer och tillverkare. Oavsett om [...]

Vad är modulen för Nylon Tips och tricks?

Inledning Nylon är en av de mest mångsidiga tekniska plasterna som används i ett brett spektrum [...].

[produkter ids="89,1119,1147″ columns="3″]

Kontakta oss