PA610 Naturligt harts

In addition to the characteristics of high strength, wear resistance and oil resistance, PA610 natural resin also has low water absorption, good dimensional stability, and excellent electrical properties.

FÅ GRATIS OFFERT

Breif Introduction of PA610 Natural Resin

PA610 natural resin, also known as polyamide 610, is a high-performance plastic known for its exceptional combination of mechanical properties. It boasts superior strength and stiffness, making it ideal for demanding applications.

PA610 shines in high-heat environments due to its excellent thermal resistance, which allows it to maintain its shape and performance at elevated temperatures. An additional benefit is its inherent flame retardancy, making it a suitable choice for safety-critical applications. Furthermore, PA610 offers good chemical resistance to various oils, greases, and fuels, enhancing its versatility. Finally, this resin exhibits good dimensional stability, minimizing warping or shrinkage over time.

Overall, PA610 natural resin is a compelling choice for components requiring a balance of strength, heat tolerance, flame retardancy, and chemical resistance.

Application Industry of PA610 Natural Resin

Rope

Bristles

Oil Pipeline

PA610 Natural Resin Data

Fysikaliska egenskaper	Metrisk	Engelska	Kommentarer
Specifik gravitation	1.08 g/cc	1.08 g/cc	ASTM D792
Absorption av vatten	0.40 %	0.40 %	24 hours at 23°C; ASTM D570
Linjär formkrympning	0.015 cm/cm @Tjocklek 3,17 mm	0.015 in/in @Tjocklek 0,125 tum	ASTM D955
	0.020 cm/cm @Thickness 6.35 mm	0.020 in/in @Thickness 0.250 in	ASTM D955

Mekaniska egenskaper	Metrisk	Engelska	Kommentarer
Hårdhet, Rockwell R	111	111	ASTM D785
Tensile Strength, Ultimate	62.1 MPa	9000 psi	ASTM D638
Töjning vid brott	90 %	90 %	ASTM D638
Elasticitetsmodul	2.76 GPa	400 ksi	ASTM D638
Flexural Yield Strength	86.2 MPa	12500 psi	ASTM D790
Böjmodul	2.07 GPa	300 ksi	ASTM D790
Compressive Yield Strength	68.9 MPa	10000 psi	ASTM D695
Izod Impact, hackad	0.481 J/cm @Tjocklek 3,17 mm	0.900 ft-lb/in @Tjocklek 0,125 tum	ASTM D256
Izod Impact, ej avbruten	6.41 J/cm @Tjocklek 3,17 mm	12.0 ft-lb/in @Tjocklek 0,125 tum	ASTM D256

Elektriska egenskaper	Metrisk	Engelska	Kommentarer
Electrical Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	ASTM D257
Dielectric Constant	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz	Dry; ASTM D150
Dielektrisk styrka	19.7 kV/mm	500 kV/in	S/T; ASTM D149
Dissipation Factor	0.020 @Frequency 1e+6 Hz	0.020 @Frequency 1e+6 Hz	Dry; ASTM D150
Arc Resistance	120 sec	120 sec	ASTM D495

Termiska egenskaper	Metrisk	Engelska	Kommentarer
CTE, linjär, Parallell till flödet	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F	ASTM D696
Termisk konduktivitet	0.216 W/m-K	1.50 BTU-in/hr-ft²-°F	Through-plane; ASTM C177
Nedböjningstemperatur vid 0,46 MPa (66 psi)	177 °C	350 °F	ASTM D648
Böjningstemperatur vid 1,8 MPa (264 psi)	62.8 °C	145 °F	ASTM D648
Brandfarlighet, UL94	V-2 @Thickness 1.59 mm	V-2 @Thickness 0.0625 in	Per testing by RTP Company; ASTM D3801

Bearbetningsegenskaper	Metrisk	Engelska	Kommentarer
Processing Temperature	274 – 293 °C	525 – 560 °F
Formtemperatur	65.6 – 107 °C	150 – 225 °F
Injection Pressure	68.9 – 124 MPa	10000 – 18000 psi

Beskrivande egenskaper
Color	Natural/Black