PA610 black resin is a type of high-performance plastic known for its durability and resistance to heat. It is a specific kind of polyamide, which is a family of engineering plastics. PA610 black resin is known for its exceptional mechanical properties, chemical resistance, and dimensional stability at elevated temperatures. This makes it a valuable material for a variety of applications in demanding environments.
PA610 black resin is a high-performance plastic belonging to the polyamide 610 family. It’s known for its exceptional mechanical properties, including strength and durability.
Additionally, it exhibits excellent resistance to chemicals and maintains its shape even at elevated temperatures. These qualities make PA610 black resin a valuable material for demanding applications across various industries. For instance, it’s commonly used in machinery manufacturing, oil storage containers, and textiles.
In the electronics industry, PA610 black resin finds uses in battery shells and instrument rails due to its durability and electrical properties. You might even encounter it in everyday objects like toothbrush bristles and cable coatings.
Fuchen always offer the PA610 resin in factory price. Let us know your requirement, we will give your our professional advice.
| Fizikinės savybės | Metrinis | Anglų kalba | Komentarai | ||
|---|---|---|---|---|---|
| Savitasis svoris | 1.08 g/cc | 1.08 g/cc | ASTM D792 | ||
| Vandens absorbcija | 0.40 % | 0.40 % | 24 hours at 23°C; ASTM D570 | ||
| Linijinis pelėsių susitraukimas | 0.015 cm/cm @Thickness 3.17 mm | 0.015 in/in @Thickness 0.125 in | ASTM D955 | ||
| 0.020 cm/cm @Thickness 6.35 mm | 0.020 in/in @Thickness 0.250 in | ASTM D955 | |||
| Mechaninės savybės | Metrinis | Anglų kalba | Komentarai | ||
| Hardness, Rockwell R | 111 | 111 | ASTM D785 | ||
| Tensile Strength, Ultimate | 62.1 MPa | 9000 psi | ASTM D638 | ||
| Pailgėjimas pertrūkio metu | 90 % | 90 % | ASTM D638 | ||
| Tamprumo modulis | 2.76 GPa | 400 ksi | ASTM D638 | ||
| Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 | ||
| Lankstumo modulis | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Compressive Yield Strength | 68.9 MPa | 10000 psi | ASTM D695 | ||
| "Izod Impact", su įpjovomis | 0.481 J/cm @Thickness 3.17 mm | 0.900 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| "Izod Impact", be įpjovos | 6.41 J/cm @Thickness 3.17 mm | 12.0 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Elektrinės savybės | Metrinis | Anglų kalba | Komentarai | ||
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | Dry; ASTM D150 | ||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | S/T; ASTM D149 | ||
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | Dry; ASTM D150 | ||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Šiluminės savybės | Metrinis | Anglų kalba | Komentarai | ||
| CTE, linijinis, lygiagretus srautui | 90.0 µm/m-°C @Temperature 20.0 °C | 50.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Šilumos laidumas | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | Through-plane; ASTM C177 | ||
| Deformacijos temperatūra esant 0,46 MPa (66 psi) | 177 °C | 350 °F | ASTM D648 | ||
| Deformacijos temperatūra esant 1,8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 | ||
| Degumas, UL94 | V-2 @Thickness 1.59 mm | V-2 @Thickness 0.0625 in | Per testing by RTP Company; ASTM D3801 | ||
| Apdorojimo savybės | Metrinis | Anglų kalba | Komentarai | ||
| Processing Temperature | 274 – 293 °C | 525 – 560 °F | |||
| Pelėsių temperatūra | 65.6 – 107 °C | 150 – 225 °F | |||
| Injection Pressure | 68.9 – 124 MPa | 10000 – 18000 psi | |||
| Aprašomosios savybės | |||||
| Color | Juoda | ||||
Įvadas Nuolat konkuruojančioje pramoninėje aplinkoje medžiagų pasirinkimas dažnai lemia inžinerinių projektų sėkmę [...]
Plastiko ir plastiko žaliavų pristatymas Kas yra plastikas ir plastiko žaliavos? Plastmasės [...]
Nailono ir PTFE pristatymas Nailonas ir PTFE (politetrafluoretilenas) yra dvi plačiai naudojamos medžiagos, kiekviena iš jų [...]
Įvadas Šiuolaikiniame pasaulyje tokios specializuotos medžiagos, kaip PA6 GB20 GF10, atlieka labai svarbų vaidmenį [...]
Plačiai naudojamas sintetinis polimeras nailonas yra populiarus dėl savo [...]
Įvadas Poliamidas 11, paprastai vadinamas PA 11, yra aukštos kokybės termoplastinė derva, gaunama iš [...]
Įvadas Šiandieninėje pramoninėje aplinkoje tinkamos medžiagos pasirinkimas gali turėti lemiamą reikšmę [...]
Poliamido ir nailono pristatymas Šiandieniniame gamybos ir gaminių dizaino pasaulyje, renkantis [...]
Bulgarian
Estonian
Turkish